High Temperature Laminating (Aluminum) - HTL-250

Category: Laminating
Ratio: 100pbw to 12pbw
Hardener: HT-106-3
Description: HTL-250 high temperature lamination resin is a tough, hard, high-impact resin offering excellent heat distortion for tools requiring elevated temperatures. HTL-250 cures at room temperature and can be used without post cure for temperatures up to 275°F. Post curing is recommended when tools will be used from 275°F to 350°F. High Temperature Cure Cycle: 1 hour @ 150°F 1 hour at 200°F 1 hour at 250°F 1 hour @ 300°F 2 hours @ 350°F
Ratio By Weight: 100pbw to 12pbw
Ratio by Volume: 5.2 to 1
Pot Life at 72° F (200 Gram Mass): 1 1/2 hours
Shore "D" Room Temperature: 85-90
Flexural Strength: 36,500
Compressive Strength: 55,000
Flexural Modulus: 1.84 x 106
Heat Distortion: 350°F
Density Resin: 12.5
Density Hardener: 7.8
Density Mixed: 12.0
Specific Gravity Resin: 1.50
Specific Gravity Hardener: .94
Specific Gravity Mixed: 1.45
Shelf Life Resin_Hardener: 1 year
Shrinkage: .002 in./in.