High Temperature Aluminum Filled Casting System - HAC-560

Category: Casting
Description: HT-9234 (Medium) approximately 2 1/2 maximum thickness Tests were determined at 1/8 inch casting that was post cured. Recommended Post Cure 1 hour at 100°F 1 hour at 150°F 1 hour at 200 °F 1 hour at 250°F 1 hour at 300°F 2 hours at 350°F 2 hours at 300 °F 2 hours at 250 °F 2 hours at 200°F 2 hours at 150 °F After oven has cooled to ambient temperature, tool can be removed.
Ratio By Weight: 100pbw to 15pbw
Ratio by Volume: 5.8( R)
Pot Life (1 lb Mass): 140 minutes
Mixed Density: 13.75 W.P.G.
Mixed Viscosity, cps: 22,400cps
Mixed Specific Gravity: 1.64 Grams/cc
Hardness: 90 Shore D
Flexural Strength: 12,700psi
Tensile Elongation at Break, %: 2.7%
Tensile Strength: 7,200 psi
Flexural Modulus: .42 x 106psi
Shrinkage: .001 in/in
Demold Time: 25-30 minutes
Co-Efficient of Thermal Expansion: 1.45x 106 in/in°F