High Temperature Aluminum Filled Casting System - HAC-560

Category: Casting
3 Hardeners Available: HT-8433, HT-9234, HT-8401
Description: HAC-560 is an aluminum filled two component, high temperature, epoxy casting system. This system can be used for injection and blow mold, molding and nesting fixtures, vacuum form molds, compression and backup for metal sprayed surfaces. *HT-8433 (Fast) Approximately 1/2" maximum thickness Recommended Post Cure 1 hour @ 100°F 1 hour @ 150°F 1 hour @200°F 1 hour @ 250°F 1 hour @ 300°F 2 hours @ 350°F 2 hours @ 300°F 2 hours @ 250°F 2 hours @ 200°F 2 hours @ 150°F After oven has cooled to ambient temperature, tool can be removed.
Ratio By Weight: 100pbw to 15pbw
Ratio by Volume: 5.8 ( R) to 1 (H)
Pot Life (1 lb Mass): 65 mins.
Mixed Viscosity, cps: 20,100 cps
Hardness Shore "D": 90
Flexural Strength: 13,000 psi
Compressive Yield Strength: 18,000 psi
Tensile Elongation at Break, %: 2.9%
Tensile Strength: 7,700psi
Flexural Modulus: .44 x 106
Density Mixed: 13.75 W.P.G.
Specific Gravity Mixed: 1.64 grams/cc
Shelf Life Resin_Hardener: 1year
Shrinkage: .002in./in.
Demold Time: 18-24 hours
Co-Efficient of Thermal Expansion: 1.51 x 106 in/in°F