High Temperature Aluminum Filled Casting System - HAC-560

Category: Casting
Description: HT8401 (slow) approximately 7" maximum thickness Tests were determined on a 1/8 inch casting that was post cured. 1 hour at 100°F 1 hour at 150°F 1 hour at 200°F 1 hour at 250°F 1 hour at 30°F 2 hours at 350°F 2 hours at 300°F 2 hours at 250°F 2 hours at 200°F 2 hours at 150°F After oven has cooled to ambient temperature, tool can be removed.
Ratio By Weight: 100pbw to 15pbw
Ratio by Volume: 5.8 ( R) to 1 (H)
Pot Life (1 lb Mass): 24 hours
Mixed Density: 13.75 W.P.G.
Mixed Viscosity, cps: 23,500 cps
Mixed Specific Gravity: 1.64 grams/cc
Hardness: 90 Shore D
Flexural Strength: 13,500psi
Compressive Yield Strength: 18,000 psi
Tensile Elongation at Break, %: 2.8%
Tensile Strength: 7,500 psi
Flexural Modulus: .46 x 106psi
Shelf Life Resin_Hardener: 1 year
Shrinkage: .001 in/in
Demold Time: 48 hours
Coefficient of Linear Thermal Expansion: 1.56 x 106 in/in °F